Fluoroplastic restoration and transformation – From adhesive tape to domes
Heat shrinkable tubing
By inserting a material into the tubing and adding heat, the tubing contracts to a snug fit granting the surface of the target material with the beneficial characteristics of fluoroplastic.
Types
- PFA heat shrinkable tubing
- FEP heat shrinkable tubing
- PTFE heat shrinkable tubing
Use
Copy machine roll covers/ communication and power cable insulation/ insulation for connectors, terminals and the like/ other
Dimension chart
| ●PFA heat shrinkable tubing TKF-200 series | ||||
| Product number | pre-contraction diameter (mm) |
final diameter (mm) |
tube thickness (mm) |
cut length (m) |
| TKF-200-1.5 | 1.8 | 1.4 | 0.2 | 1.0 |
| TKF-200-2 | 2.2 | 1.8 | 0.2 | 1.0 |
| TKF-200-2.5 | 3.0 | 2.4 | 0.2 | 1.0 |
| TKF-200-3 | 3.5 | 3.0 | 0.2 | 1.0 |
| TKF-200-4 | 4.0 | 3.5 | 0.2 | 1.0 |
| TKF-200-5 | 5.2 | 4.2 | 0.2 | 1.0 |
| TKF-200-6 | 6.0 | 5.4 | 0.2 | 1.0 |
| TKF-200-7 | 7.1 | 6.3 | 0.2 | 1.0 |
| TKF-200-9 | 9.5 | 7.5 | 0.3 | 1.0 |
| TKF-200-10 | 11.0 | 9.2 | 0.3 | 1.0 |
| TKF-200-12 | 12.9 | 10.7 | 0.3 | 1.0 |
| TKF-200-15 | 16.0 | 13.0 | 0.4 | 1.0 |
| TKF-200-17 | 19 | 16.5 | 0.5 | 1.2 |
| TKF-200-20 | 21 | 18.5 | 0.5 | 1.2 |
| TKF-200-22 | 24 | 19.5 | 0.5 | 1.2 |
| TKF-200-25 | 26 | 21.5 | 0.5 | 1.2 |
| TKF-200-27 | 30 | 24 | 0.5 | 1.2 |
| TKF-200-30 | 33 | 27 | 0.5 | 1.2 |
| TKF-200-35 | 36 | 28.5 | 0.5 | 1.2 |
| TKF-200-40 | 43 | 35 | 0.5 | 1.2 |
| TKF-200-50 | 51 | 40 | 0.5 | 1.2, 1.8 |
| TKF-200-55 | 57 | 49 | 0.5 | 1.2 |
| TKF-200-60 | 63 | 50 | 0.5 | 1.2, 1.8 |
| TKF-200-65 | 67 | 54 | 0.5 | 1.8 |
| TKF-200-70 | 71 | 61 | 0.5 | 1.8 |
| TKF-200-75 | 75 | 61 | 0.5 | 1.8 |
| TKF-200-80 | 81 | 64 | 0.5 | 1.8 |
| TKF-200-85 | 91 | 74 | 0.5 | 1.8 |
| TKF-200-95 | 98 | 82 | 0.5 | 1.8 |
| TKF-200-100 | 106 | 85 | 0.5 | 1.8, 3.6 |
| TKF-200-105 | 109 | 86 | 0.5 | 1.8 |
| TKF-200-115 | 117 | 96 | 0.5 | 1.8 |
| TKF-200-125 | 127 | 106 | 0.5 | 1.8, 3.6 |
| TKF-200-130 | 136 | 107 | 0.5 | 1.8, 3.6 |
| TKF-200-140 | 144 | 125 | 0.5 | 1.8 |
| TKF-200-150 | 154 | 125 | 0.5 | 1.8, 3.6 |
*Final contracted internal diameter measurement was obtained by heating at 200℃ for 10 minutes. Values are not guaranteed.
| ●FEP heat shrinkable tubing TKF-300 series | ||||
| Product number | pre-contraction diameter (mm) |
final diameter (mm) |
tube thickness (mm) |
cut length (m) |
| TKF-300-1.5 | 1.9 | 1.3 | 0.2 | 1.0 |
| TKF-300-2 | 2.5 | 1.8 | 0.2 | 1.0 |
| TKF-300-2.5 | 3.2 | 2.3 | 0.2 | 1.0 |
| TKF-300-3 | 3.8 | 2.7 | 0.2 | 1.0 |
| TKF-300-4 | 4.5 | 3.3 | 0.2 | 1.0 |
| TKF-300-5 | 5.5 | 4.3 | 0.2 | 1.0 |
| TKF-300-6 | 7.0 | 5.1 | 0.2 | 1.0 |
| TKF-300-7 | 7.9 | 6.0 | 0.2 | 1.0 |
| TKF-300-9 | 10.6 | 7.4 | 0.3 | 1.0 |
| TKF-300-10 | 12.5 | 8.8 | 0.3 | 1.0 |
| TKF-300-12 | 14.5 | 10.7 | 0.3 | 1.0 |
| TKF-300-15 | 17.3 | 12.8 | 0.4 | 1.0 |
| TKF-300-160 | 163 | 131 | 0.5 | 3.6 |
| TKF-300-170 | 174 | 133 | 0.5 | 3.6 |
| TKF-300-180 | 190 | 163 | 0.5 | 4.0 |
| TKF-300-200 | 206 | 164 | 0.5 | 4.0 |
| TKF-300-215 | 220 | 166 | 0.5 | 4.0 |
| TKF-300-230 | 235 | 185 | 0.5 | 4.0 |
| TKF-300-240 | 249 | 187 | 0.5 | 4.0 |
| TKF-300-250 | 259 | 206 | 0.5 | 4.0 |
| TKF-300-265 | 278 | 245 | 0.5 | 4.0 |
| TKF-300-280 | 298 | 246 | 0.5 | 4.0 |
| TKF-300-300 | 316 | 247 | 0.5 | 4.0 |
*Final contracted internal diameter measurement was obtained by heating in an electric furnace at 330℃. These values are not guaranteed.
| ●PTFE heat shrinkable tubing TKF-100 series | ||||
| Product number | pre-contraction diameter (mm) |
final diameter (mm) |
tube thickness (mm) |
cut length (m) |
| TKF-100-2 | 2.0 | 1.2 | 0.5 | 1.0 |
| TKF-100-4 | 4.0 | 2.2 | ||
| TKF-100-6 | 6.0 | 3.2 | ||
| TKF-100-8 | 8.0 | 4.2 | ||
| TKF-100-10 | 10.0 | 5.2 | ||
| TKF-100-12 | 12.0 | 6.2 | ||
| TKF-100-14 | 14.0 | 7.2 | ||
| TKF-100-16 | 16.0 | 8.2 | ||
| TKF-100-18 | 18.0 | 9.2 | ||
| TKF-100-20 | 20.0 | 10.3 | ||
| TKF-100-22 | 22.0 | 11.3 | ||
| TKF-100-24 | 24.0 | 12.3 | ||
| TKF-100-26 | 26.0 | 13.3 | ||
| TKF-100-28 | 28.0 | 14.3 | ||
| TKF-100-30 | 30.0 | 15.4 | ||
*Final contracted internal diameter measurement was obtained by heating in an electric furnace at 330℃. These values are not guaranteed.